Product Code K105 230
Product Name Composite K105, 32mm, 1500/2400 daN, 230m coil
Size 32 mm (5/4")
Weight 8.6700 KG
MOQ 60
Custom Tariff No. 3921906000
Price

Login to view Prices

ADDITIONAL PRODUCT IMAGES

 

 

Polyester Composite Strapping 32mm 

Linear strength min. 1500 daN - System strength min. 2400 daN * 

Polyester Composite belts are especially made for usage on rough environmental materials and sharp edges.  The optimise strength is the perfect base to secure the cargo.  Composite is made of parallel layers of single polyester threads laminated together with polypropylene.
It does not split, is flexible and can be used universally. The core of our composite strapping is made of untwisted polyester yarn. Due to our unique and patented process in manufacturing for untwisted yarn this strapping achieves higher strength and lower elongation. 

The special recipe of our polypropylene coating ensures an optimal compound with the polyester fibres and is at the same time resistant to most chemical solvents, caustics and acids. Due to its high abrasion protection it is well suited for products with rough surfaces and edges.

Advantages:

- High System Strength
- No damage or scratch on any surface
- No corrosion - no splicing
- Comfortable handling, easy to push under pallets
- Low investment costs  for this small, manageable system
- Retensionable & torsion absorbing
- No risk of injury for shippers and consignees in using or opening the strapping  
- Weatherproof (UV radiation)
- Easy disposable

For all our composite belts we recommend to use nitrated wire buckles. In several test they have performed better than others.

* Note:  linear and breaking strength are tested in laboratory environment. In open field applications forces and circumstances may cause different results. 

1. Technical data
Material Untwisted high tensile yarns with polypropylene (PP) cover
Paper core dimensions 200 x 190 x 5 mm
2. Required standard
Minimum linear breaking strength 1500 daN
Minimum system breaking strength 2400 daN
3. Tested data
Linear breaking strength 000 daN
System breaking strength see tested combination(s) below
4. Shipping
Custom Statistic code Tarif Number 5607500090
Place of origin China
5. Storage
Shelf live 12 month*
Conditions * when packed in box in dry and dark condition
Long Term Composite strapping will get harder/stiffer over the time, especially when exposed to UV light. But even a 5 year old belt will not loosen strength. The stiffness will make it less comfortable when pulled through the buckle, but the safety performance will NOT be affected.
Standard Container
Items per Carton 2
Cartons per Palette 30
Net weight Carton 16.90 KG
Gross weight Carton 18.60 KG
Dimension Carton 37 x 37 x 40 cm ( 0.05476m³ )
Items on Palette 60
Palette size 112*112*14.5
Total weight per Palette 597.40 KG
File Name Description File Size Mime Type
Composite Strap TUV report 2013.pdf TUV Report Composite Straps 1442755 application/pdf

Login to Download

SGS report.pdf SGS Report 2015 496329 application/pdf

Login to Download

RoHsGW85KF.pdf RoHs Report ( universal ) 266456 application/pdf

Login to Download

REACH138_COMPOSIT STRAP.pdf Reach Certificate 295604 application/pdf

Login to Download

SVHC-5S Report Composite Strap.pdf SVHC-5S Report 999737 application/pdf

Login to Download

UV composites test 688hours.pdf UV Test Report Composite 688 hours 1854099 application/pdf

Login to Download

GL GW 105 KF + B10.pdf German Lloyd Certificate 19948 application/pdf

Login to Download