Product Code | K55 |
Product Name | Composite K55, 16mm, 550/880 daN, 600m coil |
Product Size | 16 mm (5/8") |
Weight | 8.9500 KG |
MOQ | 90 |
Custom Tariff No. | 560750 |
GTIN/EAN13 | 4251858214972 |
Price |
Linear strength min. 550 daN - System strength min. 880 daN *
Polyester Composite belts are especially made for usage on rough environmental materials and sharp edges. The optimise strength is the perfect base to secure the cargo. Composite is made of parallel layers of single polyester threads laminated together with polypropylene.
It does not split, is flexible and can be used universally. The core of our composite strapping is made of untwisted polyester yarn. Due to our unique and patented process in manufacturing for untwisted yarn this strapping achieves higher strength and lower elongation.
The special recipe of our polypropylene coating ensures an optimal compound with the polyester fibres and is at the same time resistant to most chemical solvents, caustics and acids. Due to its high abrasion protection it is well suited for products with rough surfaces and edges.
Advantages:
- High System Strength
- No damage or scratch on any surface
- No corrosion - no splicing
- Comfortable handling, easy to push under pallets
- Low investment costs for this small, manageable system
- Retensionable & torsion absorbing
- No risk of injury for shippers and consignees in using or opening the strapping
- Weatherproof (UV radiation)
- Easy disposable
For all our composite belts we recommend to use nitrated wire buckles. In several test they have performed better than others.
* Note: linear and breaking strength are tested in laboratory environment. In open field applications forces and circumstances may cause different results.
1. Technical data | |
Material | Untwisted high tensile yarns with polypropylene (PP) cover |
Paper core dimensions | 200 x 190 x 5 mm |
2. Required standard | |
Minimum linear breaking strength | 550 daN |
Minimum system breaking strength | 880 daN |
3. Tested data | |
Linear breaking strength | 550 daN |
System breaking strength | see tested combination(s) below |
System breaking strength for K55+WB16G3.5 | Test 1-5 ( 894, 906, 893, 902, 898 ) Avg 899 Tested May 2017 |
4. Shipping | |
Custom Statistic code Tarif Number | 5607500090 |
Place of origin | China |
5. Storage | |
Shelf live | 12 month* |
Conditions | * when packed in box in dry and dark condition |
Long Term | Composite strapping will get harder/stiffer over the time, especially when exposed to UV light. But even a 5 year old belt will not loosen strength. The stiffness will make it less comfortable when pulled through the buckle, but the safety performance will NOT be affected. |
Standard Container | |
Items per Carton | 2 |
Cartons per Palette | 45 |
Net weight Carton | 17.10 KG |
Gross weight Carton | 18.80 KG |
Dimension Carton | 37 x 37 x 40 cm ( 0.05476m³ ) |
Items on Palette | 90 |
Palette size | 112*112*14.5 |
Total weight per Palette | 964.90 KG |
File Name | Description | File Size | Mime Type | |
---|---|---|---|---|
Composite Strap TUV report 2013.pdf | TUV Report Composite Straps | 1442755 | application/pdf | |
SGS report.pdf | SGS Report 2015 | 496329 | application/pdf | |
RoHsGW85KF.pdf | RoHs Report ( universal ) | 266456 | application/pdf | |
REACH138_COMPOSIT STRAP.pdf | Reach Certificate | 295604 | application/pdf | |
SVHC-5S Report Composite Strap.pdf | SVHC-5S Report | 999737 | application/pdf | |
UV composites test 688hours.pdf | UV Test Report Composite 688 hours | 1854099 | application/pdf | |
PrSpSh_K55.pdf | Product Data Sheet | 229258 | application/pdf | |
Test_report_for_K55+WB16G3.5.pdf | K55 Test Report May 2017 | 177362 | application/pdf |